Abstract
Many opportunities exist for flexible circuits in high-temperature applications (automotive, military, aerospace, oil and gas). Flex circuits in these applications have been hindered by a lack of materials that can survive higher temperatures. Some materials, especially some thermoset adhesives, break down over time at higher temperature, becoming brittle or losing adhesion to copper. Polyimides tend to perform much better under high temperature.
The other issue is the lack of good test methods to verify that flex materials can survive higher temperatures. Several methods for testing copper clad laminates exist, but there are very few for coverlays and bondplies. We will discuss different test methods for measuring high-temperature capability including the new IPC service temperature test. We will also report on test results for various flexible materials and our recommendations for the best flexible materials for high temperature applications. This will include development work on new flex materials for high-temperature applications.
Introduction
More applications require flexible circuits that must survive high-temperature environments. These include automotive applications near the engine, oil and gas down-hole pumps, and aerospace applications near jet engines. There have been limited test methods to determine what temperatures flexible materials can survive.
The damage caused by high-temperature environments will mainly fall in three categories: loss of adhesion between copper and dielectric, loss of adhesion between dielectric layers, and embrittlement of the dielectric layers. At the highest temperatures the copper would also become brittle, but in most cases the flexible circuit dielectrics fail first. Thermoset adhesives seem to be most sensitive to embrittlement especially compared to polyimide films which are much more resistant to high temperatures.
Read the full article here.
Editor's Note: This article originally appeared in the June 2015 issue of The PCB Magazine.
Share on:
Suggested Items
Trouble in Your Tank: Things You Can Do for Better Wet Process Control
09/11/2024 | Michael Carano -- Column: Trouble in Your TankFor 40 years, I have been involved in the printed circuit board, circuit board assembly, and semiconductor technology segments, preaching about minimizing defects and improving yields. This is especially true as technology becomes increasingly complex, and additional focus must be placed on yield improvements. Process management and wet process control must be front and center, so it’s quite interesting and timely to talk about wet process control and management for this month’s issue. This theme fits quite well with today's global events. For this industry, the technical curve has steepened dramatically in the past few years.
Atotech to Participate at KPCA Show 2024
09/03/2024 | AtotechMKS’ Atotech will participate in this year’s KPCA Show 2024 in Incheon, held at Songdo Convensia from September 4-6, 2024.
Victory Announces Breakthrough in PCB Technology with New Product Launch
08/29/2024 | openPRShenzhen Victory Electronics Technology Co., Ltd., a leader in the printed circuit board (PCB) manufacturing industry, is proud to announce the successful development of a groundbreaking new product.
Connect the Dots: Designing for Reality—Electroless Copper
08/28/2024 | Matt Stevenson -- Column: Connect the DotsRoll up your sleeves because it's time to get messy. In a recent episode of I-Connect007’s On the Line with… podcast, we discussed electroless copper deposition. This process deposits a copper layer into the through-holes and vias of what will eventually be a PCB. Electroless copper deposition feels like a black box to many people. It sort of looks like a black box, too. The boards go in one side, come out the other, and emerge differently. So, let's crack open that black box and look inside.
Maximizing ROI Through Better Wet Process Control
08/20/2024 | I-Connect007 Editorial Team“When things get out of control, the variation in your wet process begins,” says Mike Carano,. “Just because they look like good boards and may even pass electrical test, it does not necessarily mean you have good boards. Once the chemistry is headed toward the right or left side of the process control parameter cliff, the plating is compromised. If the copper is thinner than it should be, when the customer puts it into service, the board may fail after 500 cycles vs. the requisite 1,000 or 2,000 cycles. The root cause issue is that you plated 7/10ths of a mil of copper instead of one-mil of copper because you were not controlling your process. The fact that you passed your own electric test becomes inconsequential.”