In-line Solder Penetration Testing with 3D X-ray Inspection
June 10, 2015 | Andreas Turk, Goepel ElectronicEstimated reading time: 2 minutes
Through-hole technology (THT) is probably the oldest assembly technology in the field of PCB manufacturing. However, even in this modern age of surface-mounted technology (SMT), it still has its place. Even today, wired components are often assembled using wave soldering—in keeping with the tradition of times past. This has the disadvantage of requiring additional manufacturing equipment. It is therefore advisable to use reflow soldering for connectors and other wired components.
To this end, through-hole components were devised for automatic assembly and for high thermal loads in the furnace, which led to the birth of the term, through-hole reflow (THR). With this technology, it is now possible to process components in through-hole technology within the SMT process. But how can these solder joints be reliably tested? What technology is needed in order to be able to assess the solder penetration, for example?
Acceptance Criteria for THT/THR Solder Joints
Figure 1 is a schematic representation of a THT solder joint in cross-section. The solder wave flows from the solder source side to the solder target side (component side), due to capillary action. In so doing, it wets the connecting surface of the solder side, surrounds the pin and forms a solder meniscus on account of the protrusion of the pin on the solder side.
The acceptance criteria are defined in IPCA610 in order to distinguish between good and bad solder joints after successful soldering. Table 1 gives an overview of the criteria in excerpts.
It is now necessary to select testing technology which meets the specified acceptance criteria. Based on the example of a multi-row connector (Figure 2), the following table provides an overview of the test coverage of AOI and 3D AXI systems.
AOI systems are highly suited to assessment of the peripheral wetting of the pin and the sleeve and to evaluation of the wetted connecting surface on the solder side of a THT solder joint. The disadvantage of a traditional 2D AOI or an innovative 3D AOI system here, however, is that it is often only possible to assess the solder side because the pins on the component side are usually concealed by the component body itself. An assessment of the solder joints on the component side is therefore not possible with an AOI system. The solder penetration also remains hidden from traditional AOI technology.
A modern 3D X-ray system can provide a remedy. The 3D X-ray inspection not only makes the solder joints on the component side (i.e., below the component housing) visible, but is also able to calculate the solder penetration and the solder volume.
Editor's Note: This article originally appeared in the June 2015 issue of SMT Magazine.
Share on:
Suggested Items
KYZEN to Focus on Aqueous Cleaning and Stencil Cleaning at SMTA Juarez
05/20/2025 | KYZEN'KYZEN, the global leader in innovative environmentally responsible cleaning chemistries, will exhibit at the SMTA Juarez Expo and Tech Forum, scheduled to take place Thursday, June 5 at the Injectronics Convention Center in Ciudad Jarez, Chihuahua.
Koh Young Installs 24,000th Inspection System at Top 20 EMS
05/14/2025 | Koh YoungKoh Young, the global leader in True 3D measurement-based inspection and metrology solutions, proudly announces the installation of its 24,000th inspection system at a Top 20 Global EMS in Thailand.
Indium’s Karthik Vijay to Present on Dual Alloy Solder Paste Systems at SMTA’s Electronics in Harsh Environments Conference
05/06/2025 | Indium CorporationIndium Corporation Technical Manager, Europe, Africa, and the Middle East Karthik Vijay will deliver a technical presentation on dual alloy solder paste systems at SMTA’s Electronics in Harsh Environments Conference, May 20-22 in Amsterdam, Netherlands.
SolderKing Achieves the Prestigious King’s Award for Enterprise in International Trade
05/06/2025 | SolderKingSolderKing Assembly Materials Ltd, a leading British manufacturer of high-performance soldering materials and consumables, has been honoured with a King’s Award for Enterprise, one of the UK’s most respected business honours.
Knocking Down the Bone Pile: Gold Mitigation for Class 2 Electronics
05/07/2025 | Nash Bell -- Column: Knocking Down the Bone PileIn electronic assemblies, the integrity of connections between components is paramount for ensuring reliability and performance. Gold embrittlement and dissolution are two critical phenomena that can compromise this integrity. Gold embrittlement occurs when gold diffuses into solder joints or alloys, resulting in mechanical brittleness and an increased susceptibility to cracking. Conversely, gold dissolution involves the melting away of gold into solder or metal matrices, potentially altering the electrical and mechanical properties of the joint.