- News
- Books
Featured Books
- pcb007 Magazine
Latest Issues
Current IssueWet Process Control
In this issue, we examine wet processes and how to obtain a better degree of control that allows usable data to guide our decisions and produce consistently higher-quality products.
Don’t Just Survive, Thrive
If we are to be relevant and prosper during these next critical decades in electronics, we must do more than survive. As an industry, we can and must thrive. In this issue, our contributors explore these concepts meant to help you take your business to the next level.
Material Matters
Materials management is nuanced, multifaceted, and requires a holistic systems approach for business success. When building high mix, low volume, and high technology, managing materials and overall cost containment are even greater challenges.
- Articles
- Columns
Search Console
- Links
- Events
||| MENU - pcb007 Magazine
Coated Ultra-Thin Copper on Printed Circuit Laminates
July 16, 2015 | Intrinsiq Materials Inc.Estimated reading time: 5 minutes
![](https://iconnect007.com/application/files/5416/3116/8181/David_Ciufo.jpg)
Nano copper-based electronic ink and associated processing have been developed to create ultra-thin copper on flexible PCB substrates. Using a unique nanomanufacturing process, nanomaterial is created, dispersed, and sintered, resulting in copper foil of one micron or less. The process is rapid and sufficiently low-temperature to allow deposition onto temperature-sensitive substrates such as polyimide, plastic and paper. The resulting foil can be etched and processed as well as electroplated or electrolessly plated without the use of palladium.
Applying thinner copper coatings to flexible PCB substrates than are currently available will allow for much finer etch resolution and increased circuit density. The roll-to-roll lamination process in use today limits the copper foil thickness due to manufacturing and handing ultra-thin copper. A coating process eliminates these problems.
Background
High-volume roll-to-roll flexible circuit manufacturers use plasma vapor deposition (PVD) to deposit a 0.5 micron copper thin film onto unclad flexible laminates. This process provides several advantages over using copper clad laminates. One such advantage is the ability to metalize pre-drilled holes simultaneously with the surface providing good adhesion, ease of handling, and very fine feature definition. However, this is a very expensive method for applying copper and requires very specialized equipment when using today’s industry standard processes.
Nanomanufacturing
Nanomanufacturing incorporates the plasma generation process to tightly control particle size and distribution and create very pure copper. Furthermore, the manufacturing process allows the copper particles to be encapsulated with a coating, thus preventing oxidation and agglomeration. For the purpose of coating printed circuit laminates, nanomaterial particles of around 90 nm are the optimal size. Smaller particle size distributions can affect the metal loading and larger (too large) will require excessive energy to sinter. The nanoparticles can then be dispersed into solvent based inks that can be used to create very thin and uniform coatings. The ink dispersions have long shelf and pot life without special handling or storage.
Nanocoating
The deposition equipment used to create ultra-thin copper coatings includes coaters, inkjet printers, and screen printers that are commercially available and typically used in the electronics industry today. The deposition is accomplished in open air without special environmental constraints because the coating on the nanoparticles prevents oxidation. This nano technology is being used to create copper coatings onto various substrates that, in the past, could only be accomplished by processes such as PVD.
The data presented herein was derived from nanomaterial that was slot die coated on a commercial system and air-impingent dried. It has been determined that care must be taken to thoroughly dry the material once applied to the laminate to remove all residual solvent. Failure to properly dry material can result in poor adhesion after sintering and failures in post-processing. This process has been successfully demonstrated on commercially available coating and sintering equipment. It is expected that spray, dip, and other coating processes will all show similar favorable results and allow custom tailoring of coating systems to meet specific needs.
Sintering
Once deposited, the applied material is sintered either photonically or in an oven using a reduction environment. In the case of photonic sintering, a millisecond flash from a Xenon or broadband source transforms the coated material from insulting to conductive. Once sintered, the material adheres to the substrate and can be processed. For the data and images presented in this article, the coated roll of 60 feet of Kapton was then sintered using a roll-to-roll Xenon pulsed-light sintering system (Xenon Corporation S-5000).
Commercially available film coating systems would need to be retrofitted with a production quality broad band flash system or an oven system with a reducing environment to sinter the nano into pure copper. This equipment is commercially available as well. Roll-to-roll application of the nano copper can replace the previously mentioned PVD method in the manufacturing of flexible circuit materials with much thinner copper foil than is currently available.
Testing Results
Preliminary testing has been conducted by Intrinsiq to assess the quality of the ultra-thin film material and the ability to use these ultra-thin film laminates in standard PCB production processing, including pre-cleaning, imaging, etching and plating. The steps in creating the material and the steps taken in the PCB fabrication process are outlined below.
Standard polyimide flexible circuit material (0.005” thick) was coated with a one-micron dried thickness of nano copper ink in a roll-to-roll process using commercial slot die coating from the photographic film industry. The dried coating was then sintered into a 0.5-micron copper film using a production broad band flash unit designed to be integrated inline for true roll-to-roll processing. The conductivity of the resultant ultra-thin film copper was measured with a four-point probe at pre-set intervals to monitor the level of sintering during the flash process. The bulk resistivity of the sintered thin-film copper material is on the order of 10X that of bulk copper and achieved a 5B adhesion. The thin-film copper will electroplate readily due to the very low resistance of the coating as described herein. Shown in Figure 1 are examples of electrolessly plated coated copper.
Several 6” x 12” pieces (panels) were cut from the produced roll of polyimide with the ultra-thin film of copper and processed at a local PCB fabricator. The materials were pre-cleaned with standard chemistry and then laminated with photo-resist. The panels were imaged with several IPC Peel Test Coupons, tape test coupons, and standard PCB circuit patterns.Page 1 of 2
Suggested Items
Atotech to Participate at KPCA Show 2024
09/03/2024 | AtotechMKS’ Atotech will participate in this year’s KPCA Show 2024 in Incheon, held at Songdo Convensia from September 4-6, 2024.
Victory Announces Breakthrough in PCB Technology with New Product Launch
08/29/2024 | openPRShenzhen Victory Electronics Technology Co., Ltd., a leader in the printed circuit board (PCB) manufacturing industry, is proud to announce the successful development of a groundbreaking new product.
Connect the Dots: Designing for Reality—Electroless Copper
08/28/2024 | Matt Stevenson -- Column: Connect the DotsRoll up your sleeves because it's time to get messy. In a recent episode of I-Connect007’s On the Line with… podcast, we discussed electroless copper deposition. This process deposits a copper layer into the through-holes and vias of what will eventually be a PCB. Electroless copper deposition feels like a black box to many people. It sort of looks like a black box, too. The boards go in one side, come out the other, and emerge differently. So, let's crack open that black box and look inside.
Maximizing ROI Through Better Wet Process Control
08/20/2024 | I-Connect007 Editorial Team“When things get out of control, the variation in your wet process begins,” says Mike Carano,. “Just because they look like good boards and may even pass electrical test, it does not necessarily mean you have good boards. Once the chemistry is headed toward the right or left side of the process control parameter cliff, the plating is compromised. If the copper is thinner than it should be, when the customer puts it into service, the board may fail after 500 cycles vs. the requisite 1,000 or 2,000 cycles. The root cause issue is that you plated 7/10ths of a mil of copper instead of one-mil of copper because you were not controlling your process. The fact that you passed your own electric test becomes inconsequential.”
The Chemical Connection: Controlling an Alkaline Etch Bath With Low Copper Loading
08/07/2024 | Don Ball -- Column: The Chemical ConnectionThis month, I wanted to continue my discussion on how much process control is actually needed for high-density circuit production. However, in the last month, I have been called on to help with a specific process control problem: how to control an alkaline etch bath when you’re not etching much copper. This problem has been cropping up more frequently as smaller shops (and a few larger ones) concentrate on low-volume, high-value plated through-hole panels such as prototypes, resistor cores, etc.