- News
- Books
Featured Books
- smt007 Magazine
Latest Issues
Current IssueDo You Have X-ray Vision?
Has X-ray’s time finally come in electronics manufacturing? Join us in this issue of SMT007 Magazine, where we answer this question and others to bring more efficiency to your bottom line.
IPC APEX EXPO 2025: A Preview
It’s that time again. If you’re going to Anaheim for IPC APEX EXPO 2025, we’ll see you there. In the meantime, consider this issue of SMT007 Magazine to be your golden ticket to planning the show.
Technical Resources
Key industry organizations–all with knowledge sharing as a part of their mission–share their technical repositories in this issue of SMT007 Magazine. Where can you find information critical to your work? Odds are, right here.
- Articles
- Columns
Search Console
- Links
- Media kit
||| MENU - smt007 Magazine
Optimizing Solder Paste Volume for Low-Temperature Reflow of BGA Packages
July 22, 2019 | Keith Sweatman, Nihon Superior Co. LtdEstimated reading time: 4 minutes

Abstract
The need to minimize thermal damage to components and laminates, reduce warpage-induced defects to BGA packages, and save energy is driving the electronics industry towards lower process temperatures. For soldering processes, the only way that temperatures can be substantially reduced is by using solders with lower melting points. Because of constraints of toxicity, cost, and performance, the number of alloys that can be used for electronics assembly is limited, and the best prospects appear to be those based around the eutectic in the Bi-Sn system, which has a melting point of about 139°C.
Experience so far indicates that such Bi-Sn alloys do not have the mechanical properties and microstructural stability necessary to deliver the reliability required for the mounting of BGA packages. Options for improving mechanical properties with alloying additions that do not also push the process temperature back over 200°C are limited. An alternative approach that maintains a low process temperature is to form a hybrid joint with a conventional solder ball reflowed with a Bi-Sn alloy paste. During reflow, there is mixing of the ball and paste alloys. But it has been found that to achieve the best reliability, a proportion of the ball alloy has to be retained in the joint, particularly in the part of the joint that is subjected to maximum shear stress in service—which is usually the area near component side. The challenge is then to find a reproducible method for controlling the fraction of the joint thickness that remains as the original solder ball alloy.
Empirical evidence indicates that, for a particular combination of ball and paste alloys and reflow temperature, the extent to which the ball alloy is consumed by mixing with the paste alloy depends on the volume of paste deposited on the pad. If this promising method of achieving lower process temperatures is to be implemented in mass production without compromising reliability, it would be necessary to have a method of ensuring the optimum proportion of ball alloy left in the joint after reflow can be consistently maintained.
In this article, the author explains how the volume of low-melting-point alloy paste that delivers the optimum proportion of retained ball alloy for a particular reflow temperature can be determined by reference to the phase diagrams of the ball and paste alloys. The example presented is based on the equilibrium phase diagram of the binary Bi-Sn system, but the method could be applied to any combination of ball and paste alloys for which at least a partial phase diagram is available or could be easily determined.
Introduction
The dependence of the electronics industry on solder to provide the reliable connections necessary to turn a collection of individual components into a functional circuit has created an ongoing dilemma that has challenged the industry since its inception. The main consideration in the design of electronic components is functionality; whether it be to provide a specific resistance, capacitance, or inductance in passive components; logical processing in integrated circuits; and responsiveness in sensors or just electrical connectivity. A need to survive the thermal profile required to form a joint with a molten metal has been an annoying complication.
The industry has had a fairly easy start with the Sn-Pb eutectic that has a relatively low melting point of 183°C and mechanical properties and microstructural stability that have been considered to be the benchmark for reliability in service. Because of the need to maximize heat transfer into the joint to get the substrates to wetting temperature, process temperatures (e.g., soldering tool tip temperature, wave solder bath temperature, reflow oven peak temperature) had to be substantially higher than that 183°C melting point. However, with proper process control, the temperature/time profile to which the most sensitive parts of the component were exposed could be kept within a safe limit.
The move to Pb-free solder brought a renewed challenge because the alloy endorsed by IPC as “the Pb-free alloy of choice for the electronics industry”—Sn-3.0Ag-0.5Cu (SAC305)—does not start to melt until 217°C, which is 34°C higher than the melting point of the Sn-37Pb it was replacing. However, as long as the higher process temperatures could be accommodated by the use of resins and polymers that could survive the higher thermal profiles, the electronics industry was able to adapt to this new alloy.
Figure 1: Defects caused by dynamic warpage of FCBGA components during reflow soldering.
When the problem with higher process temperatures was not just thermal degradation of materials but gross deformation of component packages the challenge moved to a new level. Integrated circuit packages have evolved into complex stacks of a wide range of materials with very different coefficients of thermal expansion so that as the package heats the differential expansion of bonded layers results in warpage of the package. The problem is exacerbated by the temperature gradients that develop within the package as a result of variations in thermal conductivity and thermal mass. The extent of warpage can mean that at its peak the warpage in area array packages is sufficient to cause complete separation of joints at their extreme edges (Figure 1).
Depending on the temperature at which that peak separation is reached for a particular component, the separation can take different forms:
1. Unreflowed solder paste can be split with some adhering to the solder ball and some to the pad
2. Unreflowed solder paste adheres only to the solder ball and is lifted off the pad
3. Unreflowed solder paste adheres only to the pad with the solder ball detaching from the solder paste
To read the full article, which appeared in the July 2019 issue of SMT007 Magazine, click here.
Suggested Items
KYZEN to Highlight Stencil and Cleaning Solutions at SMTA Monterrey
03/27/2025 | KYZEN'KYZEN, the global leader in innovative environmentally friendly cleaning chemistries, will exhibit at the SMTA Monterrey Expo & Tech Forum scheduled to take place on Thursday, April 10 at the Cintermex Convention Center in Monterrey, Nuevo León. KYZEN cleaning experts will be on-site highlighting stencil cleaning chemistries KYZEN E5631J and CYBERSOLV C8882.
Indium to Showcase Proven EV Products and High-Reliability Alloys at Productronica China
03/26/2025 | Indium CorporationAs a global materials supplier and trusted partner in electric vehicle (EV) and e-Mobility manufacturing, Indium Corporation® is proud to showcase its high-reliability alloys and soldering solutions at Productronica China, March 26-28, in Shanghai, China.
SolderKing Enhances Brainboxes' Electronics Manufacturing with Expert Support and Advanced Materials
03/26/2025 | SolderKingIn modern electronics manufacturing, success relies on more than high-quality soldering materials. Technical knowledge and process expertise are just as crucial for achieving consistent results. SolderKing, a leading UK manufacturer, provides both, combining advanced consumables with specialist support to help manufacturers optimise their soldering processes.
AIM to Highlight Type 5 Solder and Other Leading Products at SMTA Monterrey Expo & Tech Forum
03/20/2025 | AIM SolderAIM Solder, a leading global manufacturer of solder assembly materials for the electronics industry, is pleased to announce its participation in the upcoming SMTA Monterrey Expo & Tech Forum taking place on April 10 at Cintermex in Monterrey, Nuevo Leon, Mexico.
Hentec Industries/RPS Automation to Showcase Valence 2508 at IPC Expo 2025
03/17/2025 | Hentec Industries/RPS AutomationThe Valence 2508 Selective Soldering System is engineered for high-mix, high-volume, advanced PCB production. It supports boards ranging from 25 x 25 mm to 559 x 559 mm (1 x 1 in. to 22 x 22 in.), with a maximum processing area of 508 x 508 mm (20 x 20 in.).