- News
- Books
Featured Books
- pcb007 Magazine
Latest Issues
Current IssueWet Process Control
In this issue, we examine wet processes and how to obtain a better degree of control that allows usable data to guide our decisions and produce consistently higher-quality products.
Don’t Just Survive, Thrive
If we are to be relevant and prosper during these next critical decades in electronics, we must do more than survive. As an industry, we can and must thrive. In this issue, our contributors explore these concepts meant to help you take your business to the next level.
Material Matters
Materials management is nuanced, multifaceted, and requires a holistic systems approach for business success. When building high mix, low volume, and high technology, managing materials and overall cost containment are even greater challenges.
- Articles
- Columns
Search Console
- Links
- Events
||| MENU - pcb007 Magazine
Characterization of PCB Material & Manufacturing Technology for High-Frequency
September 2, 2015 | E. Schlaffer, AT&S; and O. Huber, T. Faseth, and H. Arthaber, University of Technology, ViennaEstimated reading time: 15 minutes
![](https://iconnect007.com/application/files/7216/3117/0116/Figure5-thumb-31Aug15.jpg)
Abstract
Today's electronics industry is changing at a rapid pace. The root causes are manifold. The world population is growing toward eight billion, which gives rise to new challenges in terms of urbanization, mobility and connectivity. Consequently, numerous new business models for the electronic industry will develop. Connectivity will influence our lives more than ever. Concepts like Industry 4.0, Internet of Things, M2M communication, smart homes and communication in, or to cars are maturing. All these applications are based on the same demanding requirement—a considerable amount of data and increased data transfer rate. These arguments present major challenges to PCB design and manufacturing.
This paper investigates the impact of different PCB manufacturing technologies and their relation to high-frequency behavior. In the course of the paper a brief overview of PCB manufacturing capabilities will be presented. Moreover, signal losses in terms of frequency, design, manufacturing processes, and substrate materials are investigated. The aim of this paper is to develop a concept to use materials in combination with optimized PCB manufacturing processes, which allows a significant reduction of losses and increased signal quality.
First analysis demonstrates that for increased signal frequency, demanded by growing data transfer rate, the capabilities to manufacture high-frequency PCBs become a key factor in terms of losses. Base materials with particularly high-speed properties like very low dielectric constants are used for efficient design of high-speed data link lines. Furthermore, copper foils with very low treatment are to be used to minimize loss caused by the skin effect. In addition to the materials composition, the design of high-speed circuits is optimized with the help of comprehensive simulation studies.
The work on this paper focuses on requirements and main questions arising during the PCB manufacturing process in order to improve the system in terms of losses. For that matter, there are several approaches that can be used. For example, the optimization of the structuring process, the use of efficient interconnection capabilities, and dedicated surface finishing can be used to reduce losses and preserve signal integrity.
In this study, a comparison of different PCB manufacturing processes by using measurement results of demonstrators that imitate real PCB applications will be discussed. Special attention will be drawn to the manufacturing capabilities that are optimized for high-frequency requirements and focused to avoid signal loss. Different line structures like microstrip lines, coplanar waveguides, and surface integrated waveguides are used for this assessment.
This research was carried out by Austria Technologie & Systemtechnik AG (AT&S AG), in cooperation with Vienna University of Technology, Institute of Electrodynamics, Microwave and Circuit Engineering.
Introduction
Several commercially available PCB fabrication processes exist for manufacturing PCBs. In this paper two methods, pattern plating and panel plating, were utilized for manufacturing the test samples.
The first step in both described manufacturing processes is drilling, which allows connections between different copper layers. The second step for pattern plating (see figure 1) is the flash copper plating process, wherein only a thin copper skin (flash copper) is plated into the drilled holes and over the entire surface. On top of the plated copper a layer of photosensitive etch resist is laminated which is subsequently imaged by ultraviolet (UV) light using a negative film. Negative film imaging is exposing the gaps in between the traces to the UV light. In developing process the non-exposed dry film is removed with a sodium solution. After that, the whole surrounding space is plated with copper and eventually covered by tin. The tin layer protects the actual circuit pattern during etching. The pattern plating process shows typically a smaller line-width tolerance, compared to panel plating, because of a lower copper thickness before etching. The overall process tolerance for narrow dimensions in the order of several tenths of µm is approximately ± 10%.
Figure 1 (left) - Pattern plating; Figure 2 (right) - panel plating.
The second typical PCB manufacturing process is panel plating (see Figure 2). In this process, after drilling, the entire panel is plated with copper. On top of the plated copper a layer of photosensitive etch resist is laminated. After that, there is positive film imaging, whereby the actual circuit pattern is exposed to UV light. After developing, the copper is etched with a chemical wet process and in the last step the etch resist is removed and the copper structure is finished. It should be noted that in panel plating the etching is applied on the whole thickness of plated copper and copper foil. During panel plating the copper thickness varies up to ± 3% only, because of the uniform plating method. However, the distribution of the etching solution on the surface is unequal; a lower exchange of etching solution and copper occurs in the center and somewhat more on the edges of a production panel. This is called “puddling effect.” The consequences are wider lines in the center and narrower lines at the edges of each panel. The overall process tolerance for narrow dimensions in the order of several tenths of µm is approximately ± 20%.
Page 1 of 5
Suggested Items
Atotech to Participate at KPCA Show 2024
09/03/2024 | AtotechMKS’ Atotech will participate in this year’s KPCA Show 2024 in Incheon, held at Songdo Convensia from September 4-6, 2024.
Victory Announces Breakthrough in PCB Technology with New Product Launch
08/29/2024 | openPRShenzhen Victory Electronics Technology Co., Ltd., a leader in the printed circuit board (PCB) manufacturing industry, is proud to announce the successful development of a groundbreaking new product.
Connect the Dots: Designing for Reality—Electroless Copper
08/28/2024 | Matt Stevenson -- Column: Connect the DotsRoll up your sleeves because it's time to get messy. In a recent episode of I-Connect007’s On the Line with… podcast, we discussed electroless copper deposition. This process deposits a copper layer into the through-holes and vias of what will eventually be a PCB. Electroless copper deposition feels like a black box to many people. It sort of looks like a black box, too. The boards go in one side, come out the other, and emerge differently. So, let's crack open that black box and look inside.
Maximizing ROI Through Better Wet Process Control
08/20/2024 | I-Connect007 Editorial Team“When things get out of control, the variation in your wet process begins,” says Mike Carano,. “Just because they look like good boards and may even pass electrical test, it does not necessarily mean you have good boards. Once the chemistry is headed toward the right or left side of the process control parameter cliff, the plating is compromised. If the copper is thinner than it should be, when the customer puts it into service, the board may fail after 500 cycles vs. the requisite 1,000 or 2,000 cycles. The root cause issue is that you plated 7/10ths of a mil of copper instead of one-mil of copper because you were not controlling your process. The fact that you passed your own electric test becomes inconsequential.”
The Chemical Connection: Controlling an Alkaline Etch Bath With Low Copper Loading
08/07/2024 | Don Ball -- Column: The Chemical ConnectionThis month, I wanted to continue my discussion on how much process control is actually needed for high-density circuit production. However, in the last month, I have been called on to help with a specific process control problem: how to control an alkaline etch bath when you’re not etching much copper. This problem has been cropping up more frequently as smaller shops (and a few larger ones) concentrate on low-volume, high-value plated through-hole panels such as prototypes, resistor cores, etc.