- News
- Books
Featured Books
- smt007 Magazine
Latest Issues
Current IssueBox Build
One trend is to add box build and final assembly to your product offering. In this issue, we explore the opportunities and risks of adding system assembly to your service portfolio.
IPC APEX EXPO 2024 Pre-show
This month’s issue devotes its pages to a comprehensive preview of the IPC APEX EXPO 2024 event. Whether your role is technical or business, if you're new-to-the-industry or seasoned veteran, you'll find value throughout this program.
Boost Your Sales
Every part of your business can be evaluated as a process, including your sales funnel. Optimizing your selling process requires a coordinated effort between marketing and sales. In this issue, industry experts in marketing and sales offer their best advice on how to boost your sales efforts.
- Articles
- Columns
Search Console
- Links
- Events
||| MENU - smt007 Magazine
Rework and Reliability: Less is More!
September 15, 2017 | Karen Tellefsen, Alpha Assembly SolutionsEstimated reading time: 4 minutes
Circuit boards are not always perfect after reflow or wave soldering. Scrapping boards with one or two defects is expensive, so rework happens. A good concept for rework is less is more, especially less flux. Use as little rework flux as possible, as in the old Brylcreem ads, "Just a little dab'll do ya."
Liquid flux for rework is often supplied in felt-tipped applicator pens that make applying a few microliters of flux to a solder joint easy. Small squeeze bottles with tiny needle tips also work well. Paste/gel flux can be supplied in small syringes; use a small applicator tip to ensure that only a small dot of flux is applied to the rework site. Of course, using only no-clean, flux-cored solder wire without any assisting flux is the most electrochemically reliable way to do no-clean rework. The core flux in the wire will be properly heat deactivated because it will not flow until the wire is melted. Additionally, because core flux is mostly rosin or resin and hard, any activator remaining will be trapped in the flux residue. No-clean core fluxes are usually light colored and glass-like in appearance, providing nice cosmetics.
Most low solids, no-clean soldering fluxes must be exposed to soldering temperatures to become deactivated. The activator systems of these fluxes contain organic acids that remove oxides and allow solder to wet. When these organic acids are exposed to high enough temperatures for a long enough time, the activators volatilize and go away. If this doesn’t happen, the unheated or under-heated flux residues can allow electrochemical failures to occur, such as corrosion, reduction of insulation resistance, and, worst of all, electrochemical migration (Figure 1). If too much flux is applied to a rework site, some of the flux can move to nearby parts of the board that will not be exposed to the heat of the soldering tool. This often happens when flux is dispensed in large squeeze bottles with coarse tips. All those spikes in the SIR of the unheated flux are caused by the formation of dendrites between conductors.
Figure 1: SIR measurement of heated and unheated liquid, low-solids, no-clean flux.
So, how do unheated flux residues (and other contaminants) allow electrochemical problems to happen? A diagram showing these failure mechanisms is given in Figure 2. Many flux residues are hygroscopic, that is they absorb moisture from the air. This forms an electrolytic film on the board. The presence of this film allows small currents to flow between conductors at different voltages, reducing the surface insulation resistance (SIR). In some cases, the small current may cause electrolytic corrosion, which is the dissolution of metal from positively biased conductors. This rarely will cause a conductor to be completely eaten away and become an open circuit. It also can provide metal cations in the electrolyte film.
Figure 2: Electrochemical failure mechanisms caused by contaminants on circuit boards.
Now comes the worse and most destructive failure, electrochemical migration (ECM). Those metal ions in the electrolyte film will migrate to the cathodic, or negatively bias conductor because of the electrical field between the two conductors. When the metal cation gets to the cathode, it can pick up some electrons and deposit on the conductor. This deposition will usually occur at high energy locations, causing the formation of tree-like structures called dendrites. These dendrites will grow all the way to the opposing conductor causing a short circuit. These dendrites are delicate and can be destroyed by the resistive heating current flowing though the thin conductor. Noise results from the repeated forming and breaking of the dendrites, as seen in Figure 1.
Only J-STD-004B type -L0 and -L1 fluxes should be used for no-clean rework; fluxes that contain some rosin or a similar encapsulating resin, such as ROL0 and REL1, are even better. The rosin or resin in the flux will harden and help trap activators that weren’t completely heat deactivated.
Some circuit assemblers clean reworked areas with isopropyl alcohol or another solvent. For no-clean material rework, this is usually done for cosmetic reasons and more likely to hurt the electrochemical reliability than help it. No-clean fluxes are designed to be left on the circuit board. Spot cleaning may only move the dirt around. For circuits boards that are usually cleaned, spot cleaning reworked areas are not recommended. The board should be reworked with washable fluxes, and it should be put through the usual washing process again to ensure all rework fluxes are adequately removed from the board. This is especially important if the finished circuit is to be conformally coated, as coating over some flux residues can be worse than not coating at all.
In conclusion, be careful not to leave excessive or improperly heated flux residues after reworking circuit boards, or you might have more problems.
This article was originally published in the September 2017 issue of SMT Magazine.
Suggested Items
Indium Corporation Expert to Present on Pb-Free Solder for Die-Attach in Discrete Power Applications
04/30/2024 | Indium CorporationIndium Corporation Product Manager – Semiconductor Dean Payne will present at the Advanced Packaging for Power Electronics conference, hosted by IMAPS, held May 8-9 in Woburn, Massachusetts, USA.
Taiyo Circuit Automation Installs New DP3500 into Fuba Printed Circuits, Tunisia
04/25/2024 | Taiyo Circuit AutomationTaiyo Circuit Automation is proud to be partnered with Fuba Printed Circuits, Tunisia part of the OneTech Group of companies, a leading printed circuit board manufacturer based out of Bizerte, Tunisia, on their first installation of Taiyo Circuit Automation DP3500 coater.
Vicor Power Orders Hentec Industries/RPS Automation Pulsar Solderability Testing System
04/24/2024 | Hentec Industries/RPS AutomationHentec Industries/RPS Automation, a leading manufacturer of selective soldering, lead tinning and solderability test equipment, is pleased to announce that Vicor Power has finalized the purchase of a Pulsar solderability testing system.
AIM Solder’s Dillon Zhu to Present on Ultraminiature Soldering at SMTA China East
04/22/2024 | AIMAIM Solder, a leading global manufacturer of solder assembly materials for the electronics industry, is pleased to announce that Dillon Zhu will present on the topic: Ultraminiature Soldering: Techniques, Technologies, and Standards at SMTA China East. This event is being held at the Shanghai World Expo Exhibition & Convention Center from April 24-25.
AIM to Highlight NC259FPA Ultrafine No Clean Solder Paste at SMTA Wisconsin Expo & Tech Forum
04/18/2024 | AIMAIM Solder, a leading global manufacturer of solder assembly materials for the electronics industry, is pleased to announce its participation in the upcoming SMTA Wisconsin Expo & Tech Forum taking place on May 7 at the Four Points by Sheraton | Milwaukee Airport, in Milwaukee, Wisconsin.