- News
- Books
Featured Books
- smt007 Magazine
Latest Issues
Current IssueComing to Terms With AI
In this issue, we examine the profound effect artificial intelligence and machine learning are having on manufacturing and business processes. We follow technology, innovation, and money as automation becomes the new key indicator of growth in our industry.
Box Build
One trend is to add box build and final assembly to your product offering. In this issue, we explore the opportunities and risks of adding system assembly to your service portfolio.
IPC APEX EXPO 2024 Pre-show
This month’s issue devotes its pages to a comprehensive preview of the IPC APEX EXPO 2024 event. Whether your role is technical or business, if you're new-to-the-industry or seasoned veteran, you'll find value throughout this program.
- Articles
- Columns
Search Console
- Links
- Events
||| MENU - smt007 Magazine
Residual/Free TBBPA in FR-4
January 31, 2020 | Sergei Levchik, ICL-IP AmericaEstimated reading time: 4 minutes
FR-4 laminates and prepregs are important fiberglass epoxy materials for printed circuit boards (PCBs). FR-4 base materials are the most popular grade used today because they offer a cost-effective and versatile solution for electrical engineers and product designers. The FR-4 designation was created by NEMA in 1968 and denotes the laminate is flame-retarded to meet a UL94 V-0 fire rating.
Trade associations such as IEC, IPC, and JEDEC have separated FR-4 into two distinct categories based on the flame-retardant mechanism—one using brominated chemistries and the other being comprised of flame retardants, such as phosphorus, nitrogen, and synergistic fillers. FR-4 base materials using bromine as the flame-retardant mechanism are made, so the bromine-containing molecules are chemically bonded in the epoxy resin polymer. Tetra-bromobisphenol-A (TBBPA) is an important and widely used flame retardant for FR-4 base materials. Difunctional epoxy resin is reacted with TBBPA to produce oligomers of epoxy resins (Figure 1). Once cured, there is no opportunity for TBBPA to leach out.
Figure 1: Reaction of TBBPA to form epoxy polymers.
In recent years, market and regulatory interest have grown regarding potential exposure to flame retardants found in consumer and industrial goods. This has come with greater expectations that manufacturers can estimate exposures over the life cycle of their product. In some jurisdictions, there are also regulatory reporting considerations (e.g., California Prop 65) that demand a higher level of manufacturing understanding of their goods. Product designers have long presumed TBBPA is fully reacted in laminates to optimize costs and material performance and do not generally report on TBBPA levels. However, there has been little public data documenting this or defining potential “free TBBPA” within the epoxy polymer.
Testing
Laminate samples were obtained from TUC (Taiwan), Shengyi Technology (China), and Ventec (China)—all major suppliers to the electronics supply chain. The laminates tested were selected to cover both ends of the glass transition temperature (Tg) range for FR-4 products used from 140°C to over 170°C. In addition, non-brominated FR-4 laminates were tested as controls.
Laminate samples were prepared for analysis according to EPA Method 3545A (Pressurized Fluid Extraction). Method 3545 is a procedure for extracting water-insoluble or slightly water-soluble organic compounds from soils, clays, sediments, sludges, and waste solids. The method uses elevated temperature (100–180°C) and pressure (1,500–2,000 psi) and is applicable to the extraction of semi-volatile organic compounds, organophosphorus pesticides, organochlorine pesticides, chlorinated herbicides, PCBs, and PCDDs/PCDFs, which may then be analyzed by a variety of chromatographic procedures. Prepared samples were analyzed for TBBPA by EPA Method 8321B, which covers the use of high-performance liquid chromatography (HPLC), coupled with both thermospray-mass spectrometry (TS-MS) and an ultraviolet (UV) detector, for the determination of a variety of solvent-extractable nonvolatile compounds.
Before analyzing FR-4 laminate samples from the three manufacturers, the test method was independently validated with respect to TBBPA detection and quantification. Two control samples of reportedly TBBPA-free epoxy resins were obtained. One gram of each board material was ground and extracted by sonication in toluene for 90 minutes at 27°C (as described in above EPA methods) to make sample solutions. Sonication equipment was set to maximum power to ensure an aggressive extraction of any background TBBPA. Sample solutions from this process were retained and fortified with pure TBBPA at three recovery levels: 2, 4, and 10 ppm.
Results
Control and fortified samples were analyzed for TBBPA in duplicate, and the data, are shown in Table 1. The TBBPA concentration in control samples was below the 1 ppm limit of detection. TBBPA recovery in fortified sample solutions was very consistent and repeatable across all samples and, on average, was greater than 80%. There was some slight decline in percent recovery with increasing TBBPA fortification. However, in all cases, percent recoveries were well above the 70% limit of acceptability for such methods and excellent confirmation of the methods for analyzing epoxy boards.
Table 1: Fortified sample method results.
Commercially produced FR-4 laminate results are shown in Table 2. The data show all the TBBPA FR-4s had less than 1 ppm (< LOD) of “free TBBPA” demonstrating essentially complete reaction of TBBPA with the epoxy. Non-brominated samples (6, 7, 8, 9) showed the same, demonstrating the methodology consistency. The results demonstrate that the full conversion of TBBPA is independent of the glass transition temperature (Tg) of the final product and show the robustness of these production processes with respect to TBBPA conversion. Tests 10 and 11 were high-performance laminates for high-speed/high-frequency applications (not FR-4), where TBBPA-based epoxy resin was a modifying polymer in the system.
Table 2: Free-TBBPA test results.
Conclusion
In summary, it is clear FR-4 products in the market today, comprised of reacted-in brominated chemistries, do not contain “free TBBPA” after curing. As such, these products demonstrate how reactive brominated flame retardants can be used effectively to enhance the fire safety of product designs. This information will be provided to the IPC (Association Connecting Electronics Industries) for inclusion in their next revision of IPC-WP/TR-584: “IPC White Paper and Technical Report on the Use of Halogenated Flame Retardants in Printed Circuit Boards and Assemblies.”
In addition, the information will be supplied to the IEC (International Electrotechnical Commission, Geneva, Switzerland) for consideration in their standardization activities. If any manufacturers of FR-4 would like to have data on their products included in the future reports, there is still time to have FR-4 products analyzed. Please email me at Sergei.Levchic@ICL-Group.com for the contact information of the test laboratory.
I would also like to thank the analytical laboratory Applied Technical Services in Atlanta, Georgia.
Sergei Levchik is R&D director at ICL Group.
Suggested Items
I-Connect007 Editor’s Choice: Five Must-Reads for the Week
05/17/2024 | Andy Shaughnessy, Design007 MagazineThis week, trade shows are at the top of our feed, with our coverage of the Del Mar Electronics and Manufacturing Show and IPC APEX EXPO. These two longtime events are almost polar opposites in size and scope, but Del Mar seems to be expanding from its roots as a “neighborhood gathering” with its move into the Del Mar Fairgrounds. The Del Mar show always has a good “buzz factor,” which is something you can’t buy.
IPC APEX EXPO: Some Thoughts About Growth
05/16/2024 | Dan Feinberg, I-Connect007After two and a half days of wandering the aisles at IPC APEX EXPO 2024, for the first time, I almost felt like I was exploring CES. There were so many booths and exhibits that I could describe, but I’d like to focus on the growth and huge value of this event, which has expanded well beyond just the growing and impressive exhibit show floor.
IPC Raymond E. Pritchard Hall of Fame Award: Pierre-Jean Albrieux
05/10/2024 | Marcy LaRont, PCB007 MagazineCongratulations to Pierre-Jean Albrieux, who received the 2024 IPC Raymond E. Pritchard Hall of Fame Award. The award is given to individuals in recognition of the highest level of achievement, extraordinary contributions, and distinguished service to IPC and toward the advancement of the industry, including helping to create a spirit of mutual esteem, respect, and recognition among members consistent with the goals and mission of IPC.
IPC Focuses on Education and Onboarding
05/09/2024 | Andy Shaughnessy, Design007 MagazineI recently spoke with Carlos Plaza, senior director of education for IPC, about expanding educational efforts in the PCB design, fabrication, and assembly segments. As Carlos explains, PCB design is a hot topic, but onboarding may be the hottest one of all.
Real Time with… IPC APEX EXPO 2024: Industry Growth, Challenges, and Technological Advancements
05/09/2024 | Real Time with...IPC APEX EXPOEditor Nolan Johnson and Shawn DuBravac, IPC chief economist, dive into key industry topics such as growth, challenges, and technological advancements. They discuss shifts in the global competitive landscape, downstream demand, customization, and how AI is enhancing human skills. The industry outlook appears promising for both the short and long term.