Batteries with Silicon Anodes
February 15, 2019 | HZBEstimated reading time: 1 minute
In theory, silicon anodes could store ten times more lithium ions than graphite anodes, which have been used in commercial lithium batteries for many years. However, the amp-hour capacity of silicon anodes so far has been declining sharply with each additional charge-discharge cycle. Now an HZB team at BER II of the HZB in Berlin and the Institut Laue-Langevin in Grenoble has utilised neutron experiments to establish what happens at the surface of the silicon anode during charging and what processes reduce this capacity.
”With the neutron experiments and other measurements, we were able to observe how an inhibition or “blocking” layer forms on the silicon surface during charging that hinders the penetration of lithium ions,” explains HZB physicist Dr. Sebastian Risse. This 30-60 nanometre layer consists of organic molecules from the electrolyte liquid and inorganic components. When charging, the layer partially dissolves again so that the lithium ions can penetrate the silicon anode. However, energy is needed to dissolve the layer, which is then no longer available for storing. The physicists used the same electrolyte fluid in the experiment that is used in commercial lithium batteries.
Several Cycles Observed
After preliminary investigations with HZB’s BER II neutron source, the experiments at the Institut Laue-Langevin (ILL) in Grenoble provided a precise insight into the processes. ”Cold neutrons at very high flux are available at the ILL reactor. We were able to use them to non-destructively observe the silicon anode during several charge cycles,” explains Risse. Using a measuring cell developed at the HZB, physicists were able to examine the silicon anodes with neutrons during the charge-discharge cycles (in operando) and also record a number of other measurement values such as electrical resistance using impedance spectroscopy.
Efficiencies of 94%
As soon as this inhibition layer is dissolved, the efficiency of the charge-discharge cycles increases to 94 per cent (94% of the stored charge can be delivered again). This value is higher than that of lead-acid batteries (90%), but slightly lower than that of batteries employing more highly developed lithium-ion technology, which deliver up to 99.9%.
Outlook: Preventing the Blocking Layer
”We now want to investigate whether it is possible to prevent the formation of this inhibition or “blocking” layer by applying a very thin protective layer of metal oxide so that the capacity of silicon anodes decreases less over the course of many charge-discharge cycles,” says Risse.
Suggested Items
KYZEN to Focus on AQUANOX A4618 at SMTA Wisconsin Expo & Tech Forum
04/22/2024 | KYZEN'KYZEN, the global leader in innovative environmentally friendly cleaning chemistries, will exhibit at the SMTA Wisconsin Expo & Tech Forum, scheduled to take place Tuesday, May 7, 2024 at the Four Poins by Sheraton, Milwaukee Airport in Milwaukee, WI.
AIM Solder’s Dillon Zhu to Present on Ultraminiature Soldering at SMTA China East
04/22/2024 | AIMAIM Solder, a leading global manufacturer of solder assembly materials for the electronics industry, is pleased to announce that Dillon Zhu will present on the topic: Ultraminiature Soldering: Techniques, Technologies, and Standards at SMTA China East. This event is being held at the Shanghai World Expo Exhibition & Convention Center from April 24-25.
Hentec/RPS Publishes an Essential Guide to Selective Soldering Processing Tech Paper
04/17/2024 | Hentec Industries/RPS AutomationHentec Industries/RPS Automation, a leading manufacturer of selective soldering, lead tinning and solderability test equipment, announces that it has published a technical paper describing the critical process parameters that need to be optimized to ensure optimal results and guarantee the utmost in end-product quality.
Indium Corporation, Industry Partners to Showcase Products “Live@APEX”
03/26/2024 | Indium CorporationIndium Corporation®, in cooperation with its industry partners, will feature its proven solder solutions live on the show floor throughout IPC APEX Expo from Apr. 9‒11 in Anaheim, Calif., U.S.
Indium Corporation Expert to Present at iNEMI Seminar Hosted by Zestron Europe
01/25/2024 | Indium CorporationIndium Corporation Regional Technical Manager and Technologist – Advanced Applications Andreas Karch will present at iNEMI’s upcoming seminar, Humidity Robustness and Isolation Coordination for e-Mobility.