- News
- Books
Featured Books
- pcb007 Magazine
Latest Issues
Current IssueWet Process Control
In this issue, we examine wet processes and how to obtain a better degree of control that allows usable data to guide our decisions and produce consistently higher-quality products.
Don’t Just Survive, Thrive
If we are to be relevant and prosper during these next critical decades in electronics, we must do more than survive. As an industry, we can and must thrive. In this issue, our contributors explore these concepts meant to help you take your business to the next level.
Material Matters
Materials management is nuanced, multifaceted, and requires a holistic systems approach for business success. When building high mix, low volume, and high technology, managing materials and overall cost containment are even greater challenges.
- Articles
- Columns
Search Console
- Links
- Events
||| MENU - pcb007 Magazine
Material Witness: Low-Flow Prepregs–Defining the Process
March 19, 2015 | Chet GuilesEstimated reading time: 5 minutes
![](https://iconnect007.com/application/files/3516/3116/2672/chet.jpg)
One of my favorite authors once wrote about perception: “For now we see in a mirror, dimly…” speaking in an era when mirrors were at best polished metal surfaces. In the infancy of low-flow products, we used to speak about “no-flow” prepregs as if “no-flow” was sufficient definition of the product, but as we have recently pointed out in our discussions of rheology, “everything flows.” And as we consider these increasingly essential but sometimes hard-to-define products, much consideration will have to be given to what the products need to do, how they do it, how we test them, what the testing means, and how or if the testing relates meaningfully to how the products work in a PWB rigid-flex production environment.
Let’s try to define “low flow” in terms that will make sense to both suppliers and users of the products. A low-flow prepreg is a prepreg that flows sufficiently to wet out and adhere to bonding surfaces and to fill inner layer copper details, but does not flow so much as to fill in cut-out areas in a heat sink or run unevenly out of the interface between rigid and flexible elements of a rigid-flex PWB. That being said, how to define that flow quantitatively and to control it in such a way that the resulting product has wide applicability in a variety of PWB heat-sink and rigid-flex designs has been an issue with both producers and users of the products since the introduction of the concept. (My personal involvement in low flow materials began in the Early Mesozoic Period.)
How low is low flow compared to “normal” prepregs? Figure 1, the chart labeled as 35N Rheology, and Figure 2, 47N Rheology, are respectively a standard polyimide prepreg—35N—with a minimum viscosity about 800 poise at heat-up rate 5oC/minute, and a standard epoxy low-flow product—47N—with a minimum viscosity about 8000 poise at heat-up rate of 5oC/minute. As you can see, the viscosity of the low-flow product is about an order of magnitude higher than that of the full-flow prepreg.
Note also that as the heat-up rate is adjusted, the minimum viscosity of the low-flow product behaves similar to that of a standard-flow resin. As the heat-up rate increases, the minimum melt viscosity is lower, and hence, the product will flow more, all other conditions being equal. If only it were practical to use a three-temperature ramp rate test to characterize low-flow products during manufacture!
Instead, we have an IPC test procedure (IPC TM-650 2.3.17.2) that defines low flow in terms of average reduction of the diameter of a cut-out circle when the material is tested under “standard” conditions of temperature and pressure. Page 1 of 2
Suggested Items
Atotech to Participate at KPCA Show 2024
09/03/2024 | AtotechMKS’ Atotech will participate in this year’s KPCA Show 2024 in Incheon, held at Songdo Convensia from September 4-6, 2024.
Victory Announces Breakthrough in PCB Technology with New Product Launch
08/29/2024 | openPRShenzhen Victory Electronics Technology Co., Ltd., a leader in the printed circuit board (PCB) manufacturing industry, is proud to announce the successful development of a groundbreaking new product.
Connect the Dots: Designing for Reality—Electroless Copper
08/28/2024 | Matt Stevenson -- Column: Connect the DotsRoll up your sleeves because it's time to get messy. In a recent episode of I-Connect007’s On the Line with… podcast, we discussed electroless copper deposition. This process deposits a copper layer into the through-holes and vias of what will eventually be a PCB. Electroless copper deposition feels like a black box to many people. It sort of looks like a black box, too. The boards go in one side, come out the other, and emerge differently. So, let's crack open that black box and look inside.
Maximizing ROI Through Better Wet Process Control
08/20/2024 | I-Connect007 Editorial Team“When things get out of control, the variation in your wet process begins,” says Mike Carano,. “Just because they look like good boards and may even pass electrical test, it does not necessarily mean you have good boards. Once the chemistry is headed toward the right or left side of the process control parameter cliff, the plating is compromised. If the copper is thinner than it should be, when the customer puts it into service, the board may fail after 500 cycles vs. the requisite 1,000 or 2,000 cycles. The root cause issue is that you plated 7/10ths of a mil of copper instead of one-mil of copper because you were not controlling your process. The fact that you passed your own electric test becomes inconsequential.”
The Chemical Connection: Controlling an Alkaline Etch Bath With Low Copper Loading
08/07/2024 | Don Ball -- Column: The Chemical ConnectionThis month, I wanted to continue my discussion on how much process control is actually needed for high-density circuit production. However, in the last month, I have been called on to help with a specific process control problem: how to control an alkaline etch bath when you’re not etching much copper. This problem has been cropping up more frequently as smaller shops (and a few larger ones) concentrate on low-volume, high-value plated through-hole panels such as prototypes, resistor cores, etc.