- News
- Books
Featured Books
- smt007 Magazine
Latest Issues
Current IssueComing to Terms With AI
In this issue, we examine the profound effect artificial intelligence and machine learning are having on manufacturing and business processes. We follow technology, innovation, and money as automation becomes the new key indicator of growth in our industry.
Box Build
One trend is to add box build and final assembly to your product offering. In this issue, we explore the opportunities and risks of adding system assembly to your service portfolio.
IPC APEX EXPO 2024 Pre-show
This month’s issue devotes its pages to a comprehensive preview of the IPC APEX EXPO 2024 event. Whether your role is technical or business, if you're new-to-the-industry or seasoned veteran, you'll find value throughout this program.
- Articles
- Columns
Search Console
- Links
- Events
||| MENU - smt007 Magazine
Reliability Study of Bottom Terminated Components (Part 2)
July 8, 2015 | J. Nguyen, H. Marin, D. Geiger, A. Mohammed, and M. Kurwa, Flextronics InternationalEstimated reading time: 5 minutes
Failure Analysis after 1,000 thermal cycles
The components were cross sectioned after 1000 cycles. Minor cracks were observed for some BTC components. Cracks were typically initiated at the edge of the component at the component side. No crack was initiated at the void location.
Figure 1: Cross Section Images of BTC Component after 1000 Cycle.
Failure Analysis after 3,000 thermal cycles
The thermal cycle test was terminated after 3000 cycles. No failure was observed for the daisy chain components after 3000 cycles. Cracks were more pronounced at certain BTC components such as the QFN132, QFN52, QFN3550 and LGA1837 components. Most cracks were observed at the component side (Figure 2 and Figure 3).
Figure 2: Cross Section Images after 3000 Cycles for QFN52_ Non-Pre-tinned. Crack was usually seen at the component side.
Some cracks at the middle of the solder joint were also seen (Figure 4). Most of the cracks and the more severe cracks happened at the signal pins of the QFN components or when there was a large mismatch in pad design of the component. Thermal pads of QFNs and many LGA components with large pad sizes did not have major cracks after 3000 cycles.
Figure 3: Cross Section Images after 3000 Cycles for QFN88_ Pre-tinned Component. Cracks were seen at the component side and through the solder joint.
Figure 4: Cross Section Images of QFN Component After 3000 Cycles. Crack initiated at the solder joint, not at the void area.
Thermal Cycle Test Summary
There was no correlation between voiding amount at the thermal pad of the BTC and its solder joint thermal reliability. Crack were not initiated from the voids. There was a lack of evidence that voids in the thermal pads accelerated solder joint cracks.
BTC Thermal Modeling
In this study we evaluated the impact of solder voids in the thermal pad of the BTC. The experimentation was done by creating a BTC model and using a thermal simulator to evaluate the heat transfer to the ambient air and PCB. The model includes all single elements in a BTC like packaging mold material, copper pad frame, lead free solder, PCB and copper traces. Also, silicon dies with dimensions and power dissipation information are included. After validating the model by comparing the results with the thermal behavior from the component supplier several voiding conditions were created from 0% up to 98% voids by changing the thermal resistance of the tin based solder and reading the surface temperature of the package. Additional scenarios were created by changing the power dissipation of the package and plotting the results.
Component Selection
For thermal simulation, we used a DC to DC regulator QFN IR3837. This chip incorporates a PWM controller IC and two power Mosfets (control and synchronous FET). This device can operate at different currents and shows considerable power dissipation that facilitates the analysis of the impact of solder voiding.
Page 1 of 2
Suggested Items
Indium Corporation Expert to Present on Pb-Free Solder for Die-Attach in Discrete Power Applications
04/30/2024 | Indium CorporationIndium Corporation Product Manager – Semiconductor Dean Payne will present at the Advanced Packaging for Power Electronics conference, hosted by IMAPS, held May 8-9 in Woburn, Massachusetts, USA.
Taiyo Circuit Automation Installs New DP3500 into Fuba Printed Circuits, Tunisia
04/25/2024 | Taiyo Circuit AutomationTaiyo Circuit Automation is proud to be partnered with Fuba Printed Circuits, Tunisia part of the OneTech Group of companies, a leading printed circuit board manufacturer based out of Bizerte, Tunisia, on their first installation of Taiyo Circuit Automation DP3500 coater.
Vicor Power Orders Hentec Industries/RPS Automation Pulsar Solderability Testing System
04/24/2024 | Hentec Industries/RPS AutomationHentec Industries/RPS Automation, a leading manufacturer of selective soldering, lead tinning and solderability test equipment, is pleased to announce that Vicor Power has finalized the purchase of a Pulsar solderability testing system.
AIM Solder’s Dillon Zhu to Present on Ultraminiature Soldering at SMTA China East
04/22/2024 | AIMAIM Solder, a leading global manufacturer of solder assembly materials for the electronics industry, is pleased to announce that Dillon Zhu will present on the topic: Ultraminiature Soldering: Techniques, Technologies, and Standards at SMTA China East. This event is being held at the Shanghai World Expo Exhibition & Convention Center from April 24-25.
AIM to Highlight NC259FPA Ultrafine No Clean Solder Paste at SMTA Wisconsin Expo & Tech Forum
04/18/2024 | AIMAIM Solder, a leading global manufacturer of solder assembly materials for the electronics industry, is pleased to announce its participation in the upcoming SMTA Wisconsin Expo & Tech Forum taking place on May 7 at the Four Points by Sheraton | Milwaukee Airport, in Milwaukee, Wisconsin.